(Pb, La)(Zr, Sn, Ti)O-3 (PLZST) ceramic is one of the most prospective antiferroelectric (AFE) materials for variety of functional applications including energy storage and converter. Systematic structural investigation of domain structures should be of fundamental importance for understanding the structure-property relationship in AFE ceramics. In this study, the hierarchical domain structures and modulated structures correlated to the compositional variation in (Pb0.97La0.02) (Zr0.50SnxTi0.50-x)O-3 (x = 0.375, 0.45 and 0.50) were observed and in- vestigated in details by transmission electron microscopy. The PLZST ceramics show exclusively incommensurate modulated structures (IMS) whose modulation period changed from 9.37 to 6.15 and to 4.04 with increasing of the x value. The hierarchical domain structures include, in decreasing scales, AFE domains, incommensurate domains and nanodomains. The elementary domains in PLZST ceramics are pinstriped nanodomains which were formed based on IMS configuration but by frequent modulation of IMS periodicity and formation of faults. Nanodomains accumulated and then dissociated into incommensurate domains and AFE domains successively. The presently revealed structural characteristics in antiferroelectric PLZST may stimulate future researches on the evolution of IMS-based hierarchical domains under external physical fields, e.g. thermal or electrical, and their correlation to the physical performance.